Low Alloy Welding Electrodes

Engineered for Low temperature performance

ISOARC E8018-B2

PREMIUM LOW HYDROGEN TYPE 1.25% Cr – 0.5% Mo

ISOARC E9018-B3

Engineered for extreme elevated temperature performance

Chromo 2 – E7015

Low alloy type electrode engineered for elevated temperature performance

E8018-D3

High Strength Mn-Mo electrode with exceptional toughness and proven reliability

ISOARC E6013

Reliable general-purpose mild steel electrode designed for smooth arc performance, easy striking, low spatter and excellent weld appearance.

E7018-H4R C5

Premium low hydrogen electrode for critical weld integrity

Vytex Super Pro ISOARC E6013

Superior general purpose welding electrode for mild steels

E7018-1 (Isoarc 133) MMA

Low Hydrogen basic coated AC/DC electrode. The weld metal deposit is of a high metallurgical and radiographic standard complying to AWS A5.1 grade 1

General Purpose E7018 Low Hydrogen Electrode

Professional E7018 Low Hydrogen where top performance is Made Easy

E7016 – (ISOARC 102) MMA

Isoarc 102 is a specially formulated hydrogen controlled electrode, best suited to positional welding of medium carbon steel and some important low alloy steel structures.

ISOARC E7024 Iron Powder

High deposition efficiency iron powder electrode

E7018 – (ISOARC 103) MMA

ISOARC 103 is specially formulated to control heat input and reduce distortion. It is easy to use in all welding positions, has a stable arc and easily controls slag. Suitable DC only.

E6010 Pipe Rod

Cellulosic fast-freezing E6010 Pipe Electrode

ISOARC E309L-16

This is a Superior Dissimilar Metal Joining Electrode that has outstanding corrosion resistance.

ISOARC 308L-16

Premium E308L-16 electrode that has been formulated to provide excellent ductility, crack resistance and corrosion performance

ISOARC 310 – E310-16

ISOARC 310 gives a smooth flow and easy slag removal at low amperages. The weld deposit is finely rippled. For porosity free welds, use dry electrodes.

This electrode is specially formulated to weld at low amperage to ensure minimum distortion. The ISOARC 307 has good ignition and re-ignition properties, good slag removal and minimal loss through spatter.

ISOARC E316L -16

This electrode is characterised by a steady arc with very little spatter, high welding speed and easy slag removal. It produces a smooth concave weld surface in a horizontal fillet weld, which improves the resistance to fatigue.

ISOARC 168 E312-16

This highly versatile electrode is extensively used by the maintenance repair man. The high-alloy content, strength and elongation capabilities allow it to solve various problem steel joining applications.

E309L Mo 16 – 309 MOL

ISOARC 309 MOL features low-spatter loss and excellent slag removal. The work surface is smooth and finish free of undercut. The electrode is free from porosity.

Isoarc 427 Combo Impact/Abrasion Resistance

Isoarc 427 is a good combination of resistance to abrasion and impact. The wear resistance of the electrode is superior to standard chromium carbon type electrodes. Many layers can be built without cracking. This may also be used for high temperature applications. Isoarc 427 is easily weldable and can be used in all positions.

Primarc E-FeMn-C Mn-Cr-Ni Electrode

Primarc is an Austenitic, rutile basic coated high alloyed Mn-Cr Ni electrode for welding hardfacing Cr and Cr-Ni steels, dissimilar steels and cast irons.

Roller Arcing (Isoarc 453)

Isoarc 453 is an electrode for hard surfacing of steel components. This is a maintenance electrode for the hard surfacing of service sugar mill rollers. Mostly used on the rollers while the cane crushing process is taking place

Manganese Chrome HF 55 Isoarc MC

ISOARC MC is a rutile coated electrode designed for joining and surfacing 11-14% manganese steels. The deposited weld metal will work harden under impact load to a hardness of 480-590 HV. The electrode is recommended for use in the downhand position.

Nickel Manganese Isoarc 455 Fe-Mn-A

The specially formulated coating permits welding at low amperage with minimal spatter. The deposit is Austenitic, fully machinable and work hardening. Standard low hydrogen procedures should be applied.

E Fe Cr-A1 – Isoarc 438

This electrode is easy to use on AC or DC positive polarity. Bead appearance is good, and deposits are non-heat treatable. Hardness is maintained at elevated temperatures. ISOARC 438 restrikes well. The self releasing slag should be removed after each pass

ISOARC 720

Gouging Electrodes

Removing surface defects, grooving cracks for welding, chamfering out of faulty welds, surface cleaning of cast iron of poor weldability.

E St – Isoarc 270

Low hydrogen type with unusual ability to absorb impurities. Non-machinable on cast iron.

E-Ni Fe C1 – Isoarc 260

Use ISOARC 260 for cold welding all types of cast iron. Particularly recommended for pressure tight welds on heavy castings and circumferential pipe welds

E-NiC1 – Isoarc 210

Specially developed for all cold welding of cast iron, the ISOARC 210 is ideal for positional work. Extra-low heat input, high strength and fully machinable deposits result from using this electrode, extremely pure, the 210 is a low hydrogen electrode with graphite.

ENiCrFe-3 – Isoarc ENiCrFe-3

ENiCrFe-3 electrode is made on a nearly matching core wire with a basic flux system designed to produce optimum operability and demographically sound weld metal. ENiCrFe-3 is optimised for DC+ welding in all positions including pipework qualified in Asme 6G position

ENiCrMo-4 – ISOARC 276